类别 | 合**号 | 化学成分(质量分数)(%) | 密度 | 硬度 | 抗拉强度 | 冲击韧度j/cm平方 |
WC | TiC | TaC (NbC) | Co | 其他 | g/cm立方 | HRA | MPa | |
钨钴类 | YG3X | 96.5 | - | <0.5 | 3 | - | 15.0-15.3 | 91.5 | 1100 | - |
YG3 | 97 | - | - | 3 | - | 15.0-15.3 | 91 | 1200 | - |
YG4C | 96 | - | - | 4 | - | 14.9-15.2 | 89.5 | 1450 | - |
YG6X | 93.5 | - | <0.5 | 6 | - | 14.6-15.0 | 91 | 1400 | - |
YG6A | 92 | - | 2 | 6 | - | 14.7-15.1 | 91.5 | 1400 | - |
YG6 | 94 | - | - | 6 | - | 14.6-15.0 | 89.5 | 1450 | 2.6 |
YG8A | 91 | - | <1.0 | 8 | - | 14.5-14.9 | 89.5 | 1500 | - |
YG8C | 92 | - | - | 8 | - | 14.5-14.9 | 88 | 1750 | 3 |
YG8 | 92 | - | - | 8 | - | 14.5-14.9 | 89 | 1500 | 2.5 |
YG8N | 91 | - | 2.2 | 8 | - | 14.5-14.9 | 89.5 | 1500 | - |
YG10C | 90 | - | - | 10 | - | 14.3-14.6 | 86 | 2300 | - |
YG10H | 90 | - | - | 10 | - | 14.3-14.6 | 91.5 | 2200 | - |
YG11C | 89 | - | - | 11 | - | 14.0-14.4 | 86.5 | 2100 | 3.8 |
YG15 | 85 | - | - | 15 | - | 13.9-14.2 | 87 | 2100 | 4 |
YG20C | 80 | - | - | 20 | - | 13.4-13.6 | 82 | 2200 | - |
YG20 | 80 | - | - | 20 | - | 13.4-13.7 | 85.5 | 2600 | 4.8 |
YG25 | 75 | - | - | 25 | - | 12.9-13.2 | 84.5 | 2700 | |
不锈钢的发明和使用,要追溯到**次世界大战时期。英国科学家布享利·布雷尔利受英国政府军部兵工厂委托,研究武器的改进工作。那时,士兵用的**枪膛极易磨损,布雷尔利想发明一种不易磨损的合金钢。布雷尔利发明的不锈钢于1916年取得英国**权并开始大量生产,至此,从垃圾堆中偶然发现的不锈钢便风靡全球,亨利·布雷尔利也被誉为“不锈钢之父”。
在空气中或化学腐蚀介质中能够抵抗腐蚀的一种高合金钢,不锈钢是具有美观的表面和耐腐蚀性能好,不必经过镀色等表面处理,而发挥不锈钢所固有的表面性能,使用于多方面的钢铁的一种,通常称为不锈钢。
不锈钢(Stainless Steel)指耐空气、蒸汽、水等弱腐蚀介质和酸、碱、盐等化学浸蚀性介质腐蚀的钢,又称不锈耐酸钢。实际应用中,常将耐弱腐蚀介质腐蚀的钢称为不锈钢,而将耐化学介质腐蚀的钢称为耐酸钢。由于两者在化学成分上的差异,前者不一定耐化学介质腐蚀,而后者则一般均具有不锈性。不锈钢的耐蚀性取决于钢中所含的合金元素。不锈钢基本合金元素还有镍、钼、钛、铌、铜、氮等,以满足各种用途对不锈钢组织和性能的要求。不锈钢容易被氯离子腐蚀,因为铬、镍、氯是同位原素,同位原素会进行互换同化从而形成不锈钢的腐蚀。